AMBIENTUM BIOETHICA BIOLOGIA CHEMIA DIGITALIA DRAMATICA EDUCATIO ARTIS GYMNAST. ENGINEERING EPHEMERIDES EUROPAEA GEOGRAPHIA GEOLOGIA HISTORIA HISTORIA ARTIUM INFORMATICA IURISPRUDENTIA MATHEMATICA MUSICA NEGOTIA OECONOMICA PHILOLOGIA PHILOSOPHIA PHYSICA POLITICA PSYCHOLOGIA-PAEDAGOGIA SOCIOLOGIA THEOLOGIA CATHOLICA THEOLOGIA CATHOLICA LATIN THEOLOGIA GR.-CATH. VARAD THEOLOGIA ORTHODOXA THEOLOGIA REF. TRANSYLVAN
|
|||||||
The STUDIA UNIVERSITATIS BABEŞ-BOLYAI issue article summary The summary of the selected article appears at the bottom of the page. In order to get back to the contents of the issue this article belongs to you have to access the link from the title. In order to see all the articles of the archive which have as author/co-author one of the authors mentioned below, you have to access the link from the author's name. |
|||||||
STUDIA PHYSICA - Issue no. 2 / 2010 | |||||||
Article: |
ESR AND RAMAN STUDY OF V2O5 – P2O5 – BI2O3 GLASS SYSTEM. Authors: N. VEDEANU, I. ARDELEAN. |
||||||
Abstract: xV2O5(1-x) [0,8 P2O50,2 Bi2O3] glass system, with 0 ≤ x ≤ 50% mol, was prepared and investigated by ESR and Raman methods. For low content of V2O5 all the ESR spectra present a hyperfine structure typical for isolated V4+ ions. With the increasing of V2O5 content, ESR absorption signal showing hyperfine structure is covered by a broad line without hyperfine structure characteristic for clustered ions. At high V2O5 content, the vanadium hyperfine structure disappears and only the broad line can be observed in the spectra.The changes observed in the Raman spectra at low concentracion of V2O5 content (x < 10 mol %) show that vanadium oxide acts as a network modifier of the glass matrix, the bands belonging to the phosphate groups being strongly reduced. At high content of vanadium (x > 20 mol %), the vibrations characteristic for V-O-P groups appear in the spectra and the V2O5 oxide acts as a network former. Keywords: V2O5 – P2O5 – Bi2O3 glasses, ESR. |
|||||||