The summary of the selected article appears at the bottom of the page. In order to get back to the contents of the issue this article belongs to you have to access the link from the title. In order to see all the articles of the archive which have as author/co-author one of the authors mentioned below, you have to access the link from the author's name.

 
       
         
    STUDIA CHEMIA - Issue no. 4 Tom II / 2017  
         
  Article:   STUDY OF (PB, BA) - CRT GLASS WASTE BEHAVIOUR AS A PARTIAL AGGREGATE REPLACEMENT IN CEMENT MORTARS.

Authors:  LILIANA HORNEA, MARIA GOREA, NICOLAE HAR.
 
       
         
  Abstract:  

This study investigates the usability of the cathode ray tube (CRT) glass waste in a binder system. The raw materials – glass waste, river sand and cement were characterised. CRT waste was added in the amount of 30, 40 to 50 weight percent, as replacement for river sand. Glass chemical composition shows a high content in lead and alkaline oxides. Mortar prisms were prepared and kept under humid conditions. The mechanical properties were studied after 7, 28 and 90 days respectively. SEM with additional EDS was used in order to investigate the microstructure of the samples. All the samples containing glass waste achieved higher compressive strength than the control mortar. After 14, 28 and 42 days of maintaining the mortar in water no evidence of Pb was detected in the solutions.

 

Key words: cement, mortar, CRT glass waste, compressive strength

 
         
     
         
         