The summary of the selected article appears at the bottom of the page. In order to get back to the contents of the issue this article belongs to you have to access the link from the title. In order to see all the articles of the archive which have as author/co-author one of the authors mentioned below, you have to access the link from the author's name.

 
       
         
    STUDIA CHEMIA - Issue no. 2, Tom II / 2019  
         
  Article:   INFLUENCE OF THE BALL MILLING PROCESS AND AIR SINTERING CONDITIONS ON THE SYNTHESIS OF La0.7Sr0.3MnO3 CERAMICS.

Authors:  ENIKŐ BITAY, ANA-MARIA PILBAT, EMIL INDREA, IRÉN KACSÓ, MÁRTON MÁTÉ, ATTILA LEVENTE GERGELY, ERZSÉBET VERESS.
 
       
         
  Abstract:  Conventional solid-state synthesis was used to produce mixed valence manganite La0.7Ca0.3MnO3 (LCMO) from the mechanochemically activated mixture of the corresponding metal oxides. Prepared samples were characterized by XRD and SEM measurements. The results showed that it is possible to produce single phase LCMO perovskite after at least 2h of ball milling of the reaction mixture, followed by 1400ºC sintering of the dry-pressed sample pellets. The prolonged milling time as well as the higher sintering temperature leads to further stabilization of crystal structure.

Keywords: perovskite manganites, LCMO, mechanochemical synthesis, XRD, SEM, microstructural characterization
 
         
     
         
         