AMBIENTUM BIOETHICA BIOLOGIA CHEMIA DIGITALIA DRAMATICA EDUCATIO ARTIS GYMNAST. ENGINEERING EPHEMERIDES EUROPAEA GEOGRAPHIA GEOLOGIA HISTORIA HISTORIA ARTIUM INFORMATICA IURISPRUDENTIA MATHEMATICA MUSICA NEGOTIA OECONOMICA PHILOLOGIA PHILOSOPHIA PHYSICA POLITICA PSYCHOLOGIA-PAEDAGOGIA SOCIOLOGIA THEOLOGIA CATHOLICA THEOLOGIA CATHOLICA LATIN THEOLOGIA GR.-CATH. VARAD THEOLOGIA ORTHODOXA THEOLOGIA REF. TRANSYLVAN
|
|||||||
Rezumat articol ediţie STUDIA UNIVERSITATIS BABEŞ-BOLYAI În partea de jos este prezentat rezumatul articolului selectat. Pentru revenire la cuprinsul ediţiei din care face parte acest articol, se accesează linkul din titlu. Pentru vizualizarea tuturor articolelor din arhivă la care este autor/coautor unul din autorii de mai jos, se accesează linkul din numele autorului. |
|||||||
STUDIA CHEMIA - Ediţia nr.2 din 2015 | |||||||
Articol: |
INFLUENCE OF GRAIN AND CRYSTALLITE SIZE ON THE GIBBSITE TO BOEHMITE THERMAL TRANSFORMATION. Autori: . |
||||||
Rezumat:
Thermal decomposition processes of three different samples of hydrated alumina: Bayer precipitated size fractioned, Bayer precipitated ground and fine precipitated, were studied. These were investigated with special regard to evolution of boehmite. The original samples contained 75-85 wt% of gibbsite, while remaining material with gibbsite-like Al2O3-H2O ratio did not show long range order crystallinity. Decomposition reactions were observed by thermal analysis and reaction products were investigated by powder X-ray diffraction. Grain sizes were determined by laser diffraction and morphological changes of grains were observed by scanning electron microscopy. Boehmite formation is influenced mainly by grain and crystallite sizes of starting materials, while degree of crystallinity is of less importance. Transformation of gibbsite to boehmite was most pronounced in the case of coarse grains, nevertheless in fine particles boehmite evolution seemed retarded. Keywords: gibbsite decomposition, boehmite evolution, nanocrystalline boehmite, Rietveld-refinement
|
|||||||