AMBIENTUM BIOETHICA BIOLOGIA CHEMIA DIGITALIA DRAMATICA EDUCATIO ARTIS GYMNAST. ENGINEERING EPHEMERIDES EUROPAEA GEOGRAPHIA GEOLOGIA HISTORIA HISTORIA ARTIUM INFORMATICA IURISPRUDENTIA MATHEMATICA MUSICA NEGOTIA OECONOMICA PHILOLOGIA PHILOSOPHIA PHYSICA POLITICA PSYCHOLOGIA-PAEDAGOGIA SOCIOLOGIA THEOLOGIA CATHOLICA THEOLOGIA CATHOLICA LATIN THEOLOGIA GR.-CATH. VARAD THEOLOGIA ORTHODOXA THEOLOGIA REF. TRANSYLVAN ROMÂNA ENGLISH INFO PARTENERI ADRESE DE CONTACT ACCES PARTENERI FORMULAR ABONAMENT NEWSLETTER & DOWNLOAD CELE MAI NOI APARITII APARITII ÎN ANUL CURENT TOATA ARHIVA STUDIA CAUTARE ÎN ARHIVA ISTORIE PREZENT SCOP SI OBIECTIVE ECHIPA


	Rezumat articol ediţie STUDIA UNIVERSITATIS BABEŞ-BOLYAI În partea de jos este prezentat rezumatul articolului selectat. Pentru revenire la cuprinsul ediţiei din care face parte acest articol, se accesează linkul din titlu. Pentru vizualizarea tuturor articolelor din arhivă la care este autor/coautor unul din autorii de mai jos, se accesează linkul din numele autorului.


	STUDIA CHEMIA - Ediţia nr.1 din 2022

	Articol:	ELECTROCHEMICAL EVALUATION OF THE RELATIONSHIP BETWEEN THE THERMAL TREATMENT AND THE PROTECTIVE PROPERTIES OF THIN SILICA COATINGS ON ZINC SUBSTRATES. Autori: TAMARA-RITA OVÁRI, GABRIEL KATONA, GABRIELLA SZABÓ, LIANA MARIA MUREŞAN.


	Rezumat: DOI: 10.24193/subbchem.2022.1.15 Published Online: 2021-03-15 Published Print: 2021-03-30 pp. 227-243 VIEW PDF FULL PDF One of the challenges of smart and thin silica layers preparation on metallic substrates consists in the simultaneous network formation and introduction of corrosion inhibitors in it. Taking into account that both steps are affected by the temperature, it is really important to evaluate first its effect on the silica network formation. In this context, this paper aims the presentation of findings regarding the optimal heat treatment parameters in the preparation of thin silica (SiO₂) coatings on zinc. These silica layers were prepared by sol-gel method (dip-coating technique) and were tested as protective films against zinc (Zn) corrosion. After optimization of several parameters such as the drying temperature, drying duration, the corrosion resistance of the coatings was evaluated mainly by means of electrochemical methods (electrochemical impedance spectroscopy and potentiodynamic polarization). The electrochemical evaluation corroborated with morpho-structural characterization led to the conclusion that the SiO₂ coatings have better protection properties when dried at 150^°C for 1h. Keywords: zinc; sol-gel; silica coating; electrochemical impedance spectroscopy; potentiodynamic polarization curves




			Revenire la pagina precedentă